This urethane diol modifying resin imparts improved stain resistance to the forced dry (thermoset) wood clear coat formulation below.
What makes this formulation unique, is the absence of neutral-izing amines.
As a result, a free acid catalyst may be used (Nacure 155) and lower temperature cures may be achieved. A potlife of 24-48 hours is possible.
Raw Material
|
%K-Flex UD-320W
| ||
Component:
Beetle 65 Methanol S i l w e t t L-77 Rhopl ex AC-1024 Water Exxate 700 Chemcor AS-35-3 K-Flex UD-320W Nacure 155 Methanol |
0%
24.5 2.4 0.4 49.2 7.2 1.4 4.1 0.0 4.9 5.9 |
5%
24.5 2.4 0.4 44.2 9.4 1.4 4.1 2.8 4.9 5.9 |
10%
24.5 2.4 0.4 39.3 11.5 1.4 4.1 5.5 4.9 5.9 |
Formulation Procedure:
1. The components were added in the order as presented, for easier incorporation.
2. The Nacure 155 catalyst was pre-diluted with the methanol below it i n the formulation before incorporation, with a Nacure 155/Methanol ratio of 45.5/54.5. Substrate: Birch Faced Plywood Sealer: S e l f Sealed (2 Coats, 2 bakes) Sealer/Topcoat, WFT: 20-25u (0.8-1.0 mil)/Coat Sealer/Topcoat Bake: 10 min./71C (160F)
SOURCE: King Industries : Formulation WR-26